Size Selective Synthesis of Tetraoctylammonium Bromide Stabilized/Nonstabilized Sulfur Nanoparticles


Article info

2015-06-11
2015-06-30
303 - 322

Keywords

  • TEM
  • XRD
  • Sulfur.
  • Stabilizer
  • Nanoparticles
  • Size selective synthesis

Abstract

Sulfur nanoparticles (S NPs) were prepared by a quick precipitation method in the absence and presence of tetraoctylammonium bromide (TOAB) that was used as a stabilizer to control the nanoparticles size. Scanning electron microscope (SEM), transmission electron microscope (TEM) and X-Ray Diffraction (XRD) were used to characterize the obtained S NPs. The average size of S NPs was in the range 2.4 – 8.9 nm, with spherical like shape. The NPs size was controlled by changing the preparation parameters: temperatures, different acid concentrations, different acid types and the presence of TOAB stabilizer.

TOAB تحضير حبيبات نانومترية من الكبريت المثبت والغير مثبت بواسطة


معلومات المقال

2015-06-11
2015-06-30
303 - 322

الكلمات الإفتتاحية

  • TEM
  • XRD
  • Sulfur.
  • Stabilizer
  • Nanoparticles
  • Size selective synthesis

الملخص

تم في هذه الدراسة تحضير حبيبات الكبريت بحجم النانومتر وبشكل كروي وبعدة احجام مختلفة وذلك عن طريق تفاعل ترسيب الكبريت على درجات حرارة مختلفة واستخدام تراكيز وانواع من احماض مختلقة تم ذلك بوجود وعدم وجود.TOAB المثبت السطحي تم تشخيص تم تشخيص العينات المحضرة باستخدام الاجهزة التالية: XRD, TEM , SEM. اظهرت النتائج ان حجم حبيبات الكبريت المحضرة يتراوح ما بين2.4-8.9 nm.

An-Najah National University
Nablus, Palestine
P.O. Box
7, 707
Fax
(970)(9)2345982
Tel.
(970)(9)2345560
(970)(9)2345113/5/6/7-Ext. 2378
E-mail
[email protected]
Dean
Prof. Waleed Sweileh