Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene

Article info

2021-08-06
2021-12-28
91 - 108

Keywords

  • Low Density Polyethylene
  • Glass Fiber
  • Modulus
  • Acidic Whey
  • Strength Efficiency

Abstract

In order to enhance the interfacial-adhesion between short E-glass fibers and low-density polyethylene (LDPE), acidic whey; a dairy byproduct was applied as coupling agent. The fibers were immersed in acidic whey for 12, 24, 36, 48 and 60 hours. Composite materials containing 20 wt.% E- glass fibers and LDPE were prepared by extrusion process. The tensile strength and modulus of the produced composites were improved by using acidic whey, and the improvement in those properties was strongly affected by the immersion time of E-glass fibers in acidic whey. An increase of about 289%, 107%, 291% and 721% in modulus of elasticity, tensile strength, modulus efficiency and strength efficiency factors respectively were achieved after 60 hours of immersion of glass fibers in acidic whey. The effects of acidic whey on tensile properties and efficiency factors could be ascribed to the mend in interfacial-adhesion between glass fibers and LDPE polymer.

Recommended Citation

Sawalha, S., Ma’ali, R., Mushatti, H., & Makharzeh, M. (2022). Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene. An-Najah University Journal for Research - A (Natural Sciences), 36(1), 91–108. https://doi.org/10.35552/anujr.a.36.1.2005
[1]S. Sawalha, R. Ma’ali, H. Mushatti, and M. Makharzeh, “Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene,” An-Najah University Journal for Research - A (Natural Sciences), vol. 36, no. 1, pp. 91–108, Feb. 2022, doi: 10.35552/anujr.a.36.1.2005.
Sawalha, Shadi, et al. “Acidic Whey as a Novel Coupling Agent for Composites Based on E-Glass Fibers and Low-Density Polyethylene.” An-Najah University Journal for Research - A (Natural Sciences), vol. 36, no. 1, Feb. 2022, pp. 91–108. Crossref, https://doi.org/10.35552/anujr.a.36.1.2005.
1.Sawalha S, Ma’ali R, Mushatti H, Makharzeh M. Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene. An-Najah University Journal for Research - A (Natural Sciences) [Internet]. 2022 Feb;36(1):91–108. Available from: http://dx.doi.org/10.35552/anujr.a.36.1.2005
Sawalha, Shadi, Raed Ma’ali, Hussein Mushatti, and Mohammad Makharzeh. “Acidic Whey as a Novel Coupling Agent for Composites Based on E-Glass Fibers and Low-Density Polyethylene.” An-Najah University Journal for Research - A (Natural Sciences) 36, no. 1 (February 2022): 91–108. https://doi.org/10.35552/anujr.a.36.1.2005.

Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene

معلومات المقال

2021-08-06
2021-12-28
91 - 108

الكلمات الإفتتاحية

  • Low Density Polyethylene
  • Glass Fiber
  • Modulus
  • Acidic Whey
  • Strength Efficiency

الملخص

In order to enhance the interfacial-adhesion between short E-glass fibers and low-density polyethylene (LDPE), acidic whey; a dairy byproduct was applied as coupling agent. The fibers were immersed in acidic whey for 12, 24, 36, 48 and 60 hours. Composite materials containing 20 wt.% E- glass fibers and LDPE were prepared by extrusion process. The tensile strength and modulus of the produced composites were improved by using acidic whey, and the improvement in those properties was strongly affected by the immersion time of E-glass fibers in acidic whey. An increase of about 289%, 107%, 291% and 721% in modulus of elasticity, tensile strength, modulus efficiency and strength efficiency factors respectively were achieved after 60 hours of immersion of glass fibers in acidic whey. The effects of acidic whey on tensile properties and efficiency factors could be ascribed to the mend in interfacial-adhesion between glass fibers and LDPE polymer.

Recommended Citation

Sawalha, S., Ma’ali, R., Mushatti, H., & Makharzeh, M. (2022). Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene. An-Najah University Journal for Research - A (Natural Sciences), 36(1), 91–108. https://doi.org/10.35552/anujr.a.36.1.2005
[1]S. Sawalha, R. Ma’ali, H. Mushatti, and M. Makharzeh, “Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene,” An-Najah University Journal for Research - A (Natural Sciences), vol. 36, no. 1, pp. 91–108, Feb. 2022, doi: 10.35552/anujr.a.36.1.2005.
Sawalha, Shadi, et al. “Acidic Whey as a Novel Coupling Agent for Composites Based on E-Glass Fibers and Low-Density Polyethylene.” An-Najah University Journal for Research - A (Natural Sciences), vol. 36, no. 1, Feb. 2022, pp. 91–108. Crossref, https://doi.org/10.35552/anujr.a.36.1.2005.
1.Sawalha S, Ma’ali R, Mushatti H, Makharzeh M. Acidic whey as a novel coupling agent for composites based on E-Glass fibers and low-density polyethylene. An-Najah University Journal for Research - A (Natural Sciences) [Internet]. 2022 Feb;36(1):91–108. Available from: http://dx.doi.org/10.35552/anujr.a.36.1.2005
Sawalha, Shadi, Raed Ma’ali, Hussein Mushatti, and Mohammad Makharzeh. “Acidic Whey as a Novel Coupling Agent for Composites Based on E-Glass Fibers and Low-Density Polyethylene.” An-Najah University Journal for Research - A (Natural Sciences) 36, no. 1 (February 2022): 91–108. https://doi.org/10.35552/anujr.a.36.1.2005.

An-Najah National University
Nablus, Palestine
P.O. Box
7, 707
Fax
(970)(9)2345982
Tel.
(970)(9)2345560
(970)(9)2345113/5/6/7-Ext. 2628
E-mail
[email protected]
EIC
Prof. Ismail Warad

An-Najah University Journal for Research - A (Natural Sciences) by An-Najah University, Nablus, Palestine is licensed under CC BY-NC 4.0